vestiftИзвестия Национальной академии наук Беларуси. Серия физико-технических наукProceedings of the National Academy of Sciences of Belarus. Physical-technical series1561-83582524-244XThe Republican Unitary Enterprise Publishing House "Belaruskaya Navuka"vestift-253Research ArticleМАТЕРИАЛОВЕДЕНИЕ, МЕТАЛЛУРГИЯMATERIALS SCIENCES AND ENGINEERING, METALLURGYНИЗКОТЕМПЕРАТУРНОЕ МАГНИТНОЕ УПОРЯДОЧЕНИЕ В НАНОРАЗМЕРНЫХ ЗЕРНАХ Sr2FeMoO6–δLOW-TEMPERATURE MAGNETIC ORDERING IN Sr2FeMoO6–δ NANO-SIZED GRAINSЯРМОЛИЧМ. В.YARMOLICHM. V.jarmolich@physics.byКАЛАНДАН. А.KALANDAN. A.kalanda@physics.byНаучно-практический центр НАН Беларуси по материаловедениюThe Scientific and Practical Materials Research Centre of the National Academy of Sciences of Belarus201620112016031620Copyright © ЯРМОЛИЧ М.В., КАЛАНДА Н.А., 20162016ЯРМОЛИЧ М.В., КАЛАНДА Н.А.YARMOLICH M.V., KALANDA N.A.Данная работа распространяется под лицензией Creative Commons Attribution 4.0.This work is licensed under a Creative Commons Attribution 4.0 License.https://vestift.belnauka.by/jour/article/view/253

Однофазные наноразмерные порошки Sr2FeMoO6-d синтезированы цитрат-гель-методом при pH = 4, 6, 9 с различной степенью сверхструктурного упорядочения катионов Fe3+ и Mo5+ (Р = 65% д ля pH = 4, Р = 51% д ля pH = 6 и Р = 20% для pH = 9). Интервал значений размера зерен для всех порошков составляет 200-600 нм, причем наибольшее количество зерен, имеющих размер примерно 550 нм, характерно для порошков с pH = 9, а примерно 230 нм для pH = 4. Установлено уменьшение величины P с ростом рН, что указывает на увеличение числа кластеров –Fe2+-О2-Fe2+- с антипараллельным распределением спинов железа, приводящее к снижению суммарного магнитного момента и значений температур Кюри. В порошках, синтезированных при pH = 4, количество низкоразмерных зерен значительно больше, чем в порошках при pH = 6, 9, что обусловило их большую намагниченность при Т = 4,2-19 K.

Single-phase nanosized Sr2FeMoO6-d powders were synthesized by the citrate-gel-method at pH = 4, 6, 9, with various degrees of superstructural ordering of Fe3+ and Mo5+ (P = 65% for pH = 4, P = 51% for pH = 6 and P = 20 % for pH = 9). Grain size of the powders are in the range of 200–600 nm. With that, the largest number of grains having a size of 550 nm was characteristic for powders with pH = 9 and 230 nm for pH = 4. It was established that the value of P decreases with increasing pH, which indicates an increase in the number of –Fe2+-О2--Fe2+- clusters with antiparallel distribution of iron spins which leads to a decrease in the total magnetic moment and the Curie temperature. In powders with pH = 4 the number of low dimensional grain is significantly larger than in powders with pH = 6 and 9, which led to their large magnetization value at T = 4,2- 19 K.

ферромолибдат стронцияцитрат-гель-методсверхструктурное упорядочениенамагниченностьсуперпарамагнитное состояниеstrontium ferromolybdatecitrate-gel-methodsuperstructural orderingmagnetizationsuperparamagnetic stateReferencesInfluence of preparation method on SrMoO4 impurity content and magnetotransport properties of double perovskite Sr2FeMoO6 polycrystals / C. L. Yuan [et al.] // Sol. Stat. Comm. – 2004. – N 129(9). – P. 551–554.Influence of preparation method on SrMoO4 impurity content and magnetotransport properties of double perovskite Sr2FeMoO6 polycrystals / C. L. Yuan [et al.] // Sol. Stat. Comm. – 2004. – N 129(9). – P. 551–554.Interplay between phase formation mechanisms and magnetism in the Sr2FeMoO6 metal-oxide compound / N. Kalanda [et al.] // Cryst. Res. Technol. – 2011. – Vol. 6. – N 5. – P. 463–469.Interplay between phase formation mechanisms and magnetism in the Sr2FeMoO6 metal-oxide compound / N. Kalanda [et al.] // Cryst. Res. Technol. – 2011. – Vol. 6. – N 5. – P. 463–469.Inhomogeneous magnetic state in the Sr2FeMoO6–d double perovskite / N. A. Kalanda [et al.] // Science of Advanced Materials. – 2015. – Vol. 7. – P. 446–454.Inhomogeneous magnetic state in the Sr2FeMoO6–d double perovskite / N. A. Kalanda [et al.] // Science of Advanced Materials. – 2015. – Vol. 7. – P. 446–454.Magnetic properties of fine SFMO particles: Superparamagnetism / T. Suominen [et al.] // J. Magn. Magn. Mater. – 2007. – Vol. 309. – P. 278–284.Magnetic properties of fine SFMO particles: Superparamagnetism / T. Suominen [et al.] // J. Magn. Magn. Mater. – 2007. – Vol. 309. – P. 278–284.Absence of tunnel magnetoresistance in Sr2FeMoO6-based magnetic tunnel junctions / T. Fix [et al.] // Chem. Phys. Lett. – 2007. – Vol. 434. – P. 276–279.Absence of tunnel magnetoresistance in Sr2FeMoO6-based magnetic tunnel junctions / T. Fix [et al.] // Chem. Phys. Lett. – 2007. – Vol. 434. – P. 276–279.Coey, J. M. D. Magnetism and Magnetic Materials/ J. M. D. Coe. – Cambridge University Press: New York, – 2010. – P. 231–263.Coey, J. M. D. Magnetism and Magnetic Materials/ J. M. D. Coe. – Cambridge University Press: New York, – 2010. – P. 231–263.

The authors declare that there are no conflicts of interest present.