Application of iron-containing materials and organic contaminants as charge at grey iron melting

New scientific data are presented considering chemical hardening of metal-containing wastes with organic contaminants (oily cast iron turnings, scale, and polishing sludge with oil content up to 10 mass%. If oils are oxidized and their components are simultaneously transformed into cleaner condition by baling (without high pressure), it is accompanied by formation of basic salts such as (MgOH)₃PO₄ or (MgOHAlO₂ + (MgOH)₂SiO₃) at co-mixing of excessive amounts of clay (alkaline), lack of magnesite and the acidic medium. When iron contacts the acid, light acid film is decomposed, and a denser phosphate film is formed (phosphate), it promotes good adhesion and provides the required strength of bales. Introducing up to 30% of bales with metal-containing wastes with organic contaminants into charge of furnace according to the developed technology provides an increase up to 70% of the amount of pearlite in the metal base of iron while its dispersion is improving up to 1.4Pd -0.3Pd, and a significant amount of fine hardening phases is formed.

железоуглеродистые сплавы, чугун, металлосодержащие отходы с органическим загрязнителем, техногенные отходы изделий из полимерных материалов, структурообразование, микросостав и морфология неметаллических включений, iron-carbon alloys, cast iron, metal-containing wastes with organic contaminants, industrial waste products from polymer materials, structure formation, microcomposition and morphology of non-metallic inclusions

1. Ласковнёв, А. П. Создание литейных материалов из техногенных отходов/ А.П. Ласковнёв, А. И. Гарост // Весці НАН Беларусі. Сер.фіз.-тэхн. навук. - 2015. - № 3. - С. 88-95.

2. Ласковнёв, А. П. Устойчивость состава и структуры материала к воздействию факторов окружающей среды при создании полиакрилонитрильных охлаждающих сред / А. П. Ласковнёв, А. И. Гарост, Е. В. Кривоносова // Науков1 нотатки. Луцький нацюнальний техшчний университет. Млжвуз1вський зб1рник. - 2015. - Вш. 49. -С. 89-96.

3. Harast, A. I. The Casting Technologies Focused on the Use of Industrial Waste and Semiprocessed Products Related to Engineering Industries/A. I.Harast // Journal of Multidisciplinary Engineering Science and Technology (JMEST), ISSN: 3159-0040. -2015. -Vol. 2, issue 5.- P. 914-918.

4. Ласковнёв, А. П. Многофункциональные (износостойкие и антифрикционные) покрытия на изделиях из чугуна / А. П. Ласковнёв, А. И. Гарост, А. И. Покровский // Литье и металлургия. - 2015. - № 2. - С. 89-94.

5. Конюх, В. Я. Газокислородная плавка металла /В. Я. Конюх. - Киев: Наукова думка, 1979. - 160 с.

6. Гарост, А. И. Железоуглеродистые сплавы: структурообразование и свойства / А. И. Гарост. - Минск: Беларуская навука, 2010. - 252 с.

7. Способ выплавки чугуна: пат. 14183 Респ. Беларусь: МПК (2006) C21C1/00, C21C5/00, F23G5/027 / А. И. Гарост; заявитель УО «Бел. гос. технол. ун-т». - № а20091272; заявл. 31.08.2009; опубл. 30.04.2011 // Афщыйны бюлетэнь / Нац. цэнтр штэлект. уласнасщ. - 2010. - № 1.

8. Способ выплавки чугуна и способ выплавки стали: пат. 11641 Респ. Беларусь: МПК (2006) C 21 C 1/00, C 21 C 5/00, F 23 G 5/027 / А. И. Гарост; заявитель УО «Бел.гос. технол. ун-т». - № а20050280; заявл. 24.03.2005; опубл. 30.12.2006 // Афщыйны бюлетэнь / Нац. цэнтр штэлект. уласнасщ. - 2009. - № 1.