Mechanism of formation of aluminum-copper solid and liquid-metal solutions during alloy←→ melt phase transformation
Abstract
Methods of X ray analysis and scanning electron microscopy have been used for investigating the structure of rapidly quenched Al-12 mass % Cu alloy after carrying out the annealing treatments in the temperature range of existence of solid and liquid phases. It is established that a rapid heating of microcastings results in dissolution and dispersion of Q-phase plate like particles in a-solid solution. The formation of liquid phase at the temperatures lower than eutectic one occurs by the mechanism of metastable contact melting that prevails over the mechanism of monotropic melting. The liquid phase is suspension of ultradisperse particles of Q-phase in metastable aluminumcopper melt.
References
1. Попель П. С., Матвеев В. М., Чикова О. А. // Расплавы. 1995. № 2. С. 81-86.
2. Замятин В. М., Насыйров Я. А., Топчий А. Л. // Расплавы. 1990. № 4. С. 99-102.
3. Гаврилин И. В. Плавление и кристаллизация металлов и сплавов. Владимир, 2000.
4. Бродова И. Г., Попель П. С., Барбин Н. М., Ватолин Н. А. Исходные сплавы как основа формирования структуры и свойств алюминиевых сплавов. Екатеринбург, 2005.
5. Попель П. С., Чикрва О. А., Бродова И. Г. // Физика металлов и металловедение. 1992. № 9. С. 111-115.
6. Баум Б. А., Тягунов Г. В., Барышев Е. Е. // Расплавы.1999. № 5. С. 32-34.
7. Laine E. S. U., Hiltunen E. S., Heinonen M. H. // Acta Met. 1980. Vol. 28. P. 1565-1569.
8. Вол А. Е. Строение и свойства металлических систем. М., 1959. Т.1.
9. Буйнов Н. Н., Захарова Р. Р. Распад металлических твердых растворов. М., 1964.
10. Малин Дж. Кристаллизация. М., 1965.
11. Черемской П. Г., Сизов В. В., Бехтин В. И. Поры в твердом теле. М., 1977.
12. Залкин В. М. Природа эатектических сплавов. М., 1987.
13. Ивлиев В. Н. // Журн. физ. химии. 1983. № 3. С. 455-457.
Review
Views: 629
Email this article 