Formation of zinc oxide single-crystal nanostructures on lithium niobate substrates and metal films
Abstract
The results of the rod nanostructures synthesis and porous zinc oxide films on lithium niobate substrates by hydrothermal method and on the metal films by electrochemical deposition are presented. It was shown that hydrothermal method can be successfully used for formation of the hexagonal rod structures with a diameter up to 100 nm on the single crystal substrates. Electrochemical synthesis method is promising for formation of zinc oxide rod structures with a diameter up to 1 ^m on gold films and porous films on aluminum conductive layers. It was established that increasing of the solution concentration for the electrochemical synthesis method increases diameter of zinc oxide rod nanostructures. The obtained results can be used to select the optimal process parameters of zinc oxide nanostructures synthesis for subsequent application in micro-, nanoelectronics and photovoltaics
About the Authors
G. A. Pashkevich
Научно-исследовательский институт прикладной электроники Национального технического университета Украины «Киевский политехнический институт»
Belarus
Belarus
A. T. Orlov
Научно-исследовательский институт прикладной электроники Национального технического университета Украины «Киевский политехнический институт»
Belarus
Belarus
V. O. Ulianova
Научно-исследовательский институт прикладной электроники Национального технического университета Украины «Киевский политехнический институт»
Belarus
Belarus
O. V. Bogdan
Научно-исследовательский институт прикладной электроники Национального технического университета Украины «Киевский политехнический институт»
Belarus
Belarus
References
1. Jagadish C. Zinc Oxide Bulk, Thin Films and Nanostructures: Processing, Properties, and Applications. Elsevier, Amsterdam, 2006.
2. Ozgur U. et al. // Proc. IEEE 98. 2010. P. 1255-1268.
3. Banerjee D. // Appl. Phys. 2005. Vol. A80. P. 749-752.
4. Park W. I. et al. // Appl. Phys. Lett. 2002. Vol. 80, N 22. P. 4232-4234.
5. Sun Y. et al. // Chem. Phys. Lett. 2004. Vol. 396, N 1-3. P. 21-26.
6. Zeng H. B. et al. // Sci. Adv. Mater. 2010. Vol. 2, N 3. P. 336-358.
7. Hyunghoon Kim et al. // Electronic Materials Letters. 2009. Vol. 5, N 3. P. 135-138.
8. Bai Shr-Nan // J Mater Sci: Mater Electron. 2011. Vol. 22, N 4. P. 339-344.
9. Jia Guozhi et al. // Digest Journal of Nanomaterials and Biostructures. 2012. Vol. 7, N 1. P. 261-267.
10. Orlov A. T. et al. // 23rd Intern. Crimean Conf. «Microwave & Telecommunication Technology». 2013. P. 830-832.
11. Orlov A. et al. // Proc. 2013 IEEE XXXIII Intern. Scientific Conf. Electronics and Nanotechnology (ELNANO). 2013. P. 25-27.
Review
Views: 452
Email this article 