Structure and properties of rapidly solidifing foils Sn – 14 at.% In – 6.5 at.% Zn

The results of studies of the effect of ultra-high cooling rates of the melt equal to 10⁵ K/s on the phase composition, microstructure, grain structure and mechanical properties of the Sn – 14 at.% In – 6.5 at.% Zn alloy are presented. To prepare the samples, the rapid quenching from the melt technique was used. A drop of melt was injected onto the inner surface of a rapidly rotating copper cylinder and solidifing in the form of a foil with a thickness of 30–90 μm. Investigations of the phase composition, carried out by the method of Х-ray diffraction analysis, made it possible to establish that the foil consists of a solid solution of zinc in the γ -phase (Sn4In) and zinc. Observations of the microstructure of the foil using scanning electron microscopy showed that the decomposition of a supersaturated solid solution proceeds at room temperature with the release of dispersed zinc particles. The character of the grain structure and texture of the foil is studied by the electron backscatter diffraction technique. A mechanism of the formation of elongated grains is proposed, which consists in the fact that at a high solidification rate, comparable to the rate of movement of the melt over the surface of the mold, grain growth can occur not only in the direction opposite to the direction of heat removal, but also in the direction of movement of the spreading. The formation of the preferred growth of grains, in which the most closely-packed plane (0001) is parallel to the foil surface, provides the maximum rate of decrease in the enthalpy of the alloy during crystallization. The features of the influence of the microstructure and grain structure on the mechanical properties of the foil are revealed. The microhardness of the rapidly solidifing Sn – 14 at.% In – 6.5 at.% Zn alloy is 105 MPa. The stress–strain curve of the Sn – 14 at.% In – 6.5 at.% Zn foil, obtained at room temperature, has a shape specific for the stress–strain curve of metals at high temperatures, which is due to the low melting point of the γ-phase.

high-speed solidification, tin, indium, zinc, microstructure, mechanical properties

1. Lyakishev N. P., ed. State Diagrams of Binary Metal Systems: a Reference. Vol. 1. Moscow, Mashinostroenie Publ., 2001. 872 p. (in Russian).

2. Vasil’ev V. A., Mitin B. S., Pashkov I. N., Serov N. M., Skuridin A. A., Lukin A. A., Yakovlev V.B. High-speed Solidification of Melts (Theory, Technology and Materials). Moscow, Intermet inzhiniring Publ., 1998. 400 p. (in Russian).

3. Miroshnichenko I. S. Quenching from a Liquid State. Moscow, Metallurgiya Publ., 1982. 168 p. (in Russian).

4. Shepelevich V. G. Fast Solidified Fusible Alloys. Minsk, Belarusian State University, 2015. 192 p. (in Russian).

5. Saltykov S. A. Stereometric Metallography. Moscow, Metallurgiya Publ., 1970. 272 p. (in Russian).

6. Shepelevich V. G., Siutsova P. A., Neumerzhytskaya E. Yu., Gutko E. S. Kuckorecko K. V. Texture of rapidly solidified foils of aluminium and its alloys. Journal of Alloys and Compounds, 2005, vol. 403, no. 1–2, pp. 267–269. https://doi.org/10.1016/j.jallcom.2004.07.089

7. Shakhrai O. N., Shepelevich V. G. The texture of rapidly solidified foils of lead and its alloys. Vestsi Natsyyanal’nai akademii navuk Belarusi. Seryya fizika-technichnych navuk = Proceedings of the National Academy of Sciences of Belarus. Physical-technical series, 2004, no. 3, pp. 32–34 (in Russian).

8. Li D. Y., Szpunar J. A. A possible role for surface packing density in the formation of {111} texture in solidified FCC metals. Journal of Materials Science Letters, 1994, vol. 13, no. 21, pp. 1521–1523. https://doi.org/10.1007/BF00626496

9. Ziegler H. Some Extremum Principles in Irreversible Thermodynamics with Application to Continuum Mechanics. Amsterdam, North-Holland, 1963. VII + 193 s.

10. Gusakova O., Shepelevich V. The influence of melt flow on grain structure of tin and its alloys produced by ultrafast quenching from the melt. IOP Conf. Series: Materials Science and Engineering, 2017, vol. 192, p. 012015-1-6. https://doi.org/10.1088/1757-899x/192/1/012015

11. Bernshtejn M. L. Structure of Deformed Metals. Мoscow, Metallurgiya Publ., 1977. 432 p. (in Russian).

12. Shepelevich V. G., Metto Ye. S., Gusakova S. V., Gusakova O. V. Structure and mechanical properties rapidly solidified foils of the Sn – 14 at.% In – 6.5 at.% Zn. Priborostroenie-2017: materialy 10-i Mezhdunarodnoi nauchnotekhnicheskoi konferentsii, Minsk, 1–3 noyabrya 2017 g. [Instrument Making-2017: Materials of the 10th International Scientific and Technical Conference, Minsk, November 1–3, 2017]. Minsk, BNTU, 2017, pp. 244–246 (in Russian).